What Is The Stress - Strain Relation For Rubber?

1.	What Is The Stress - Strain Relation For Rubber?
Answer» Rubber can be pulled to several times its length and STILL it returns to its ORIGINAL shape. There is no well DEFINED PLASTIC flow region. Rubber just breaks when deforming forces are removed. Rubber can be pulled to several times its length and still it returns to its original shape. There is no well defined plastic flow region. Rubber just breaks when deforming forces are removed.

Answer»

Rubber can be pulled to several times its length and STILL it returns to its ORIGINAL shape. There is no well DEFINED PLASTIC flow region. Rubber just breaks when deforming forces are removed.

Rubber can be pulled to several times its length and still it returns to its original shape. There is no well defined plastic flow region. Rubber just breaks when deforming forces are removed.

Discussion

No Comment Found

Related InterviewSolutions

To Keep A Piece Of Paper Horizontal, You Should Blow Over, Not Under It. Why?
What Is Bernoulli’s Theorem In Terms Of Various Heads?
What Is Bernoulli’s Theorem?
How Will You Find Whether The Flow Of A Liquid Through A Pipe Is Steady Or Turbulent?
What Is A Stream Line?
What Is Turbulent Flow?
What Is Steady Flow?
What Is “rate Of Flow” Of A Liquid Through A Pipe?
What Is The Essential Condition So That A Liquid Is Able To Flow Through A Pipe?
Do Gases Also Possess Viscosity?

What Is The Stress - Strain Relation For Rubber?

Discussion

No Comment Found

Related InterviewSolutions

Reply to Comment