In cold rolling process, no any residual stresses are induced in the material during the operation.(a) True(b) FalseI had been asked this question in examination.Origin of the question is Cold Rolling topic in chapter Mechanical Working of Metals of Casting-Forming-Welding II

In cold rolling process, no any residual stresses are induced in the m

1.	In cold rolling process, no any residual stresses are induced in the material during the operation.(a) True(b) FalseI had been asked this question in examination.Origin of the question is Cold Rolling topic in chapter Mechanical Working of Metals of Casting-Forming-Welding II
Answer» RIGHT option is (B) False Best explanation: In cold ROLLING process, strain HARDENING occurs during the expansion or compression of metal plate, which increases the value of flow stress, so that the required rolling force increases, which further lead to inducing of residual stresses in the material. This residual stresses then can be removed from the material by the annealing process.

Discussion

No Comment Found

Related InterviewSolutions

The dislocation density of the material increases during the process of cold rolling or work hardening.(a) True(b) FalseThis question was addressed to me in homework.This interesting question is from Cold Rolling in portion Mechanical Working of Metals of Casting-Forming-Welding II
In metal forming, deep drawing process is completely different from wire drawing process.(a) True(b) FalseThe question was posed to me in unit test.Enquiry is from Deep Drawing in section Mechanical Working of Metals of Casting-Forming-Welding II
In deep or cup drawing, maximum tensile stress is caused near the end of punch.(a) True(b) FalseI got this question in semester exam.Question is taken from Deep Drawing in portion Mechanical Working of Metals of Casting-Forming-Welding II
Fabrication methods of materials greatly affect the geometry of defects in the material.(a) True(b) FalseThe question was asked during an interview.The origin of the question is Metallurgical Aspects topic in portion Mechanical Working of Metals of Casting-Forming-Welding II
Which of the following methods of heat treatment is best suitable for treating the output of cold rolling?(a) Quenching(b) Case hardening(c) Annealing(d) Cyanide hardeningThis question was addressed to me at a job interview.Query is from Cold Rolling in section Mechanical Working of Metals of Casting-Forming-Welding II
The difference between the radius of punch and die basically represents occupied length of metal in the die cavity.(a) True(b) FalseThe question was asked in quiz.This intriguing question originated from Deep Drawing in division Mechanical Working of Metals of Casting-Forming-Welding II
In deep drawing, the metal at the bottom side of the punch only undergoes longitudinal tensile stresses.(a) True(b) FalseThis question was posed to me in examination.This intriguing question comes from Deep Drawing topic in section Mechanical Working of Metals of Casting-Forming-Welding II
In fatigue failure, the behaviour of material under cyclic load generally differs from that under monotonic load.(a) True(b) FalseThe question was posed to me during an interview for a job.This interesting question is from Metallurgical Aspects topic in chapter Mechanical Working of Metals of Casting-Forming-Welding II
Necking phenomena do not occur in the process of a cup or deep drawing.(a) True(b) FalseThis question was posed to me at a job interview.My question comes from Deep Drawing in section Mechanical Working of Metals of Casting-Forming-Welding II
Corrosion fatigue is very small problem and it has negligible effects on the material properties.(a) True(b) FalseThis question was addressed to me in an online quiz.This intriguing question comes from Metallurgical Aspects topic in portion Mechanical Working of Metals of Casting-Forming-Welding II

In cold rolling process, no any residual stresses are induced in the material during the operation.(a) True(b) FalseI had been asked this question in examination.Origin of the question is Cold Rolling topic in chapter Mechanical Working of Metals of Casting-Forming-Welding II

Discussion

No Comment Found

Related InterviewSolutions

Reply to Comment