In the heat treatment, normalizing method cannot be applicable for non-ferrous materials.(a) True(b) FalseI had been asked this question in examination.The above asked question is from Method of Heat Treatment topic in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II

In the heat treatment, normalizing method cannot be applicable for non

1.	In the heat treatment, normalizing method cannot be applicable for non-ferrous materials.(a) True(b) FalseI had been asked this question in examination.The above asked question is from Method of Heat Treatment topic in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Answer» The correct answer is (a) True Best explanation: The objective of normalizing is to remove internal stresses from the MATERIAL being treated. Normalizing can be applicable to FERROUS materials, but it cannot be used for TREATING non-ferrous materials. In normalizing, the metal is heated to a HIGHER temperature and then it is removed from the FURNACE for air cooling.

Discussion

No Comment Found

Related InterviewSolutions

What is the amount of tungsten used in HPF steel?(a) Less than 0.03%(b) Less than 0.02%(c) Less than 0.04%(d) Less than 0.05%I got this question at a job interview.I want to ask this question from Inverse Rate Curves for Steel in section Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Which of the following is also called as diffusion annealing?(a) Isothermal annealing(b) Process annealing(c) Homogenizing(d) Spheroidise annealingThe question was asked in examination.My question is based upon Annealing and Normalizing topic in division Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Annealing is a fast process.(a) True(b) FalseThis question was posed to me by my school principal while I was bunking the class.I would like to ask this question from Annealing and Normalizing topic in portion Heat treatment of Metals and Alloys of Casting-Forming-Welding II
In full annealing, the metal cannot be buried in which of the following materials?(a) Sand(b) Lime(c) Ashes(d) Manganese powderI have been asked this question in an interview for job.This interesting question is from Annealing and Normalizing topic in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II
How much is the Brinell hardness of sorbite?(a) 250(b) 350(c) 450(d) 550The question was asked by my college director while I was bunking the class.Question is from Transformation in Steel in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Alpha iron exists only in high temperature and pressure conditions.(a) True(b) FalseI got this question by my school teacher while I was bunking the class.This interesting question is from Cooling Curve for Pure Iron topic in portion Heat treatment of Metals and Alloys of Casting-Forming-Welding II
What is the kind of lattice in a gamma iron?(a) Face centered cubic(b) Body centered cubic(c) Hexagonal closely packed(d) Tetragonal closely packedThis question was addressed to me by my college director while I was bunking the class.Question is taken from Cooling Curve for Pure Iron in portion Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Heat treatment is a process which alters the mechanical properties of metal by changing the product shape.(a) True(b) FalseThis question was posed to me in an online quiz.My question is taken from Method of Heat Treatment in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II
Which of the following is not an objective of annealing?(a) Softening of steel(b) Hardening of steel(c) Increase ductility(d) Relieve internal stressThe question was posed to me by my college professor while I was bunking the class.The doubt is from Annealing and Normalizing in division Heat treatment of Metals and Alloys of Casting-Forming-Welding II
What is the amount of silicon used in HPF steel?(a) Less than 0.30%(b) Less than 0.20%(c) Less than 0.40%(d) Less than 0.50%This question was addressed to me in final exam.My question is from Inverse Rate Curves for Steel in section Heat treatment of Metals and Alloys of Casting-Forming-Welding II

In the heat treatment, normalizing method cannot be applicable for non-ferrous materials.(a) True(b) FalseI had been asked this question in examination.The above asked question is from Method of Heat Treatment topic in chapter Heat treatment of Metals and Alloys of Casting-Forming-Welding II

Discussion

No Comment Found

Related InterviewSolutions

Reply to Comment