1.	The second order Bragg diffraction of X-rays with l =1.0 A0 froma set of parallel planes in a metal occurs at an angle of 600.The distance between the scattering planes in the crystal is
Answer» The second order Bragg diffraction of X-rays with l =1.0 A⁰froma set of parallel planes in a metal occurs at an angle of 60⁰.The distance between the scattering planes in the crystal is

Discussion

No Comment Found

Related InterviewSolutions

If this is Energy vs Dihedral angle graph of Butane, then I,II and III are respectively :
When limestone is heated, quicklime is formed according to the equation. CaCO3(s)⇌CaO(s)+CO2(g)The experiment was carried out in the temperature range 800−900oC, Equilibrium constant Kp follows the relation. log Kp=7.282−8500Twhere, T is temperature in Kelvin. At what temperature the decomposition will give CO2(g) at 1 atm?
Which of the following solutions will have the highest boiling point?
In a compound oxide ions are present in CCP. 16 th of the tetrahedral voids are occupied cation A and 13 rd of the octahedral voids are occupied by cation B. What is the formula of the compound and what are the charges on A and B respectively.
Number of equivalent(s) of HI required for a complete reaction with the above compound is/are
Which of the following reactions will not give 2-methyl-2-phenylpropane?
An aqueous solution of BaCl2 (1.28gm in 100gm of water)boils at 100.0832∘ at 1 atm. Calculate the degree of dissociation. ( Kb of water is 0.512 k/m)
50 mL of H2 gas diffuses through a small hole from a vessel in 20 min. Time taken by 40 mL of O2 gas to diffuse under similar conditions will be :
Which of the following is not isoelectronic series?
The rate constant for a reaction depends upon each of the following, EXCEPT: