Which of the following method is the best approach to report the results of the pitting corrosion test?(a) Reporting the number of pits per unit area(b) Reporting maximum depth of a pit(c) Reporting average depth of pits(d) Reporting weight loss of a metalThe question was posed to me in final exam.This is a very interesting question from Testing in division Corrosion Testing of Corrosion Engineering

Which of the following method is the best approach to report the resul

1.	Which of the following method is the best approach to report the results of the pitting corrosion test?(a) Reporting the number of pits per unit area(b) Reporting maximum depth of a pit(c) Reporting average depth of pits(d) Reporting weight loss of a metalThe question was posed to me in final exam.This is a very interesting question from Testing in division Corrosion Testing of Corrosion Engineering
Answer» Right ANSWER is (B) REPORTING maximum depth of a pit The best explanation: Pitting corrosion is one of the types of corrosion in which PERFORATED metal is formed DUE to the formation of holes on the metal surface. The best way to report the corrosion testing of pitting is to report the maximum depth of a pit.

Discussion

No Comment Found

Related InterviewSolutions

Which of the following is/are the corrosion testing’s for stainless steels?(a) Warren test(b) Streicher test(c) Huey test(d) Warren test, Streicher test and huey testThe question was posed to me during an interview.Query is from Testing topic in division Corrosion Testing of Corrosion Engineering
Which of the following units are used in terms of penetration of pits on a metal?(a) Milligram sq. decimeter per day (MDD)(b) Mils per year (MPY)(c) Both MDD and MPY(d) Neither MDD nor MPYThis question was addressed to me in homework.The query is from Testing in division Corrosion Testing of Corrosion Engineering
Calculate the corrosion penetration rate of iron that corroding at an electrochemical corrosion rate of 1 microampere/sq. centimeters?(a) 0.212 mpy(b) 0.11 mpy(c) 0.46 mpy(d) 0.64 mpyI have been asked this question during an interview.My query is from Testing in section Corrosion Testing of Corrosion Engineering
Which of the following is/are the factors that affect corrosion testing?(a) Temperature(b) Dissolved oxygen(c) Nature of metal(d) Temperature, dissolved oxygen, and nature of metalThis question was posed to me in quiz.This question is from Testing in portion Corrosion Testing of Corrosion Engineering
The corrosion mechanism of polymeric and metallic materials are the same in all corrosive environments.(a) True(b) FalseI have been asked this question in exam.My doubt is from Testing in chapter Corrosion Testing of Corrosion Engineering
Which of the following metals in which corrosion decreases with an increase in temperature in oxygenated corrosive solutions?(a) Copper and its alloys(b) Steels(c) Cast irons(d) Aluminum and its alloysI got this question during an online exam.The question is from Testing topic in division Corrosion Testing of Corrosion Engineering
Which of the following type of corrosion tests are usually best and more desirable?(a) Laboratory testing(b) Pilot-plant testing(c) Both laboratory and pilot-plant testing(d) Neither laboratory nor pilot-plant testingThe question was asked by my school teacher while I was bunking the class.This intriguing question originated from Testing in division Corrosion Testing of Corrosion Engineering
What is meant by nomography for corrosion rates?(a) Formula oriented method to find corrosion rate(b) A rapid and ready conversion table for various corrosion rate units(c) Schematic arrangement of corrosion data with the change in temperature and concentration(d) A specific corrosion rate measurement methodThis question was addressed to me during an online interview.Question is taken from Testing in section Corrosion Testing of Corrosion Engineering
Which of the following is/are the causes for the bond rupturing in polymers?(a) Chemical reaction (oxidation)(b) Heat(c) Radiation (sunlight)(d) Chemical reaction, heat, and radiationI got this question in a job interview.Enquiry is from Testing topic in portion Corrosion Testing of Corrosion Engineering
A standard surface condition is also desirable and necessary to facilitate comparison with other results.(a) True(b) FalseThis question was posed to me in my homework.This is a very interesting question from Testing in chapter Corrosion Testing of Corrosion Engineering

Discussion

No Comment Found

Related InterviewSolutions

Reply to Comment